We are professional manufacture of stainless steel welded pipe and seamless pipe in China.
Grade:
304(0Cr18Ni9 ) 304L(00Cr19Ni10 ) 321(1Cr18Ni9Ti )
321(0Cr18Ni10Ti)316(0Cr17Ni12Mo2)316L(00Cr17Ni14Mo2)316L (00Cr18Ni12Mo2Ti)310S(0Cr25Ni20) 310S(1Cr25Ni20Si2)904L(00Cr20Ni25Mo4)201
Size:
Diameter range: 6mm-630mm
Wall thickness: 0.5mm-60mm
Length: The max is 12m or as customers' required
Processing:
Cold drawn or cold rolled
Grade |
Chemical Composition |
Others |
Mechanical Properties, min |
ASTM |
|
|
Tensile Strength Ksi (Mpa) |
Yeild Point Ksi (Mpa) |
Elongation % min |
Hardness Test Max |
|
C |
Si. |
Mn |
P |
S |
Ni |
Cr |
Mo |
|
HB |
HRB |
|
max |
max |
max |
max |
max |
|
|
|
|
min |
min |
min |
|
|
304 |
0.08 |
0.75 |
2.00 |
0, 045 |
0.03 |
8.00~11.00 |
18.00~20.00 |
- |
- |
75(515) |
30(205) |
35 |
192 |
90 |
304 L |
0.035 |
0.75 |
2.00 |
0, 045 |
0.03 |
8.00~13.00 |
18.00-20.00 |
- |
- |
70(485) |
25(170) |
35 |
192 |
90 |
309 |
0.15 |
0.75 |
2.00 |
0, 045 |
0.03 |
12.00~15.00 |
22.00~24.00 |
- |
- |
75(515) |
30(205) |
35 |
192 |
90 |
310 |
0.15 |
0.75 |
2.00 |
0, 045 |
0.03 |
19.00~22.00 |
24.00~26.00 |
- |
- |
75(5150 |
30(205) |
35 |
192 |
90 |
316 |
0.08 |
0.75 |
2.00 |
0, 045 |
0.03 |
11.00~14.00 |
16.00~18.00 |
2.00~3.00 |
- |
75(515) |
30(205) |
35 |
192 |
90 |
316 L |
0.035 |
0.75 |
2.00 |
0, 045 |
0.03 |
10.00~15.00 |
16.00~18.00 |
2.00~3.00 |
- |
70(485) |
25(170) |
35 |
192 |
90 |
316 Ti |
0.08 |
0.75 |
2.00 |
0, 045 |
0.03 |
11.00~14.00 |
16.00~18.00 |
2.00~3.00 |
Ti: 5xC% ~0.75 |
75(515) |
30(205) |
35 |
192 |
90 |
317 |
0.08 |
0.75 |
2.00 |
0, 045 |
0.03 |
11.00~14.00 |
18.00~20.00 |
3.00~4.00 |
- |
75(515) |
30(205) |
35 |
192 |
90 |
321 |
0.08 |
0.75 |
2.00 |
0, 045 |
0.03 |
9.00~13.00 |
17.00~20.00 |
- |
Ti: 5 x C% ~ 0.70 B |
75(515) |
30(205) |
35 |
192 |
90 |
321 H |
0.04~ 0.10 |
0.75 |
2.00 |
0, 045 |
0.03 |
9.00~13.00 |
17.00~20.00 |
- |
Ti: 4 x C% ~0.60 |
75(515) |
30(205) |
35 |
192 |
90 |
347 |
0.08 |
0.75 |
2.00 |
0, 045 |
0.03 |
9.00~13.00 |
17.00~20.00 |
- |
Nb + Ta: 10 x C% ~1.00 |
75(515) |
30(205) |
35 |
192 |
90 |
347 H |
0.04~ 0.10 |
0.75 |
2.00 |
0, 045 |
0.03 |
9.00~13.00 |
17.00~20.00 |
- |
Nb +Ta: 8 XC% ~ 1.0 |
75(515) |
30(205) |
35 |
192 |
90 |
410 |
0.15 |
1.00 |
1.00 |
0, 040 |
0.03 |
0.75 |
11.5~13.5 |
- |
- |
60(415) |
30(205) |
20 |
207 |
95 |
430 |
0.12 |
1.00 |
1.00 |
0, 040 |
0.03 |
0.75 |
16.00~18.00 |
- |
- |
60(415) |
35(240) |
20 |
190 |
90 |